Title: Influência do resfriamento da porcelana com e sem leucita na referência à fratura de sistemas com infraestrutura em zircônia
Other Titles: Porcelain cooling influence with and without leucite in reference to fracture systems infrastructure Zirconia
???metadata.dc.creator???: Meirelles, Potira Dalques 
???metadata.dc.contributor.advisor1???: Benetti, Paula
???metadata.dc.contributor.advisor-co1???: Borba, Márcia
???metadata.dc.description.resumo???: Este estudo investigou a influência do protocolo de resfriamento da porcelana com e sem leucita na resistência à fratura aplicadas sobre zircônia. Foram testadas as hipóteses de que (1) a resistência e confiabilidade da porcelana contendo leucita são maiores do que a da porcelana sem leucita quando aplicadas sobre a zircônia, e (2) o protocolo de resfriamento lento resulta em maior resistência da porcelana que o resfriamento rápido para ambos os sistemas testados. Foram confeccionadas 120 barras de zircônia (0,8 de espessura), que foram recobertas com 1 mm de espessura de porcelana (dimensão total de 1,8mm x 4mm x 16 mm). As barras foram divididas em quatro grupos (n=30), para aplicação das diferentes porcelanas (com ou sem leucita) e protocolos de resfriamento (rápido ou lento). Os espécimes foram submetidos ao teste de resistência à flexão em 3 pontos até o primeiro sinal de fratura, mantendo a superfície da porcelana sob tração. Os dados foram analisados por ANOVA de dois fatores e teste de Tukey (95%). Foram realizadas as análises de Weibull e de fratura. Os resultados mostraram que a resistência à fratura do sistema contendo porcelana com leucita foi semelhante ao sistema sem leucita (p=0,718). O protocolo de resfriamento aplicado não modificou a resistência à flexão dos grupos (p = 0,761). As hipóteses do estudo foram rejeitadas, pois a presença de leucita e o resfriamento não alteraram significativamente a resistência à fratura e confiabilidade dos sistemas
Abstract: This study investigated the influence of porcelain cooling protocol with and without leucite in fracture resistance applied on zirconia. We tested the hypothesis that (1) the strength and reliability of the porcelain containing leucite are larger than the porcelain without leucite when applied on zirconia, and (2) slow cooling protocol results in greater strength than china cooling fast for both tested systems. Were prepared zirconia rods 120 (0.8 thick) were coated with 1 mm thick porcelain (total size 1.8 mm x 16 mm x 4mm). The bars were divided into four groups (n = 30) for application of different porcelains (with or without leucite), and cooling systems (fast or slow). The specimens were subjected to flexural strength testing in 3 points to the first sign of fracture, keeping the surface of the porcelain under traction. Data were analyzed by two-way ANOVA and Tukey test (95%). Analysis of Weibull and fracture were performed. The results showed that the resistance to fracture system containing leucite porcelain was similar to the system without leucite (p = 0.718). The cooling protocol used did not modify the flexural strength of the two groups (p = 0.761). The study hypotheses were rejected, since the presence of leucite and cooling did not significantly alter the fracture strength and reliability of the systems
Keywords: Cerâmica odontológica
Óxido de zircônio
Dental ceramics
Zirconium oxide
???metadata.dc.subject.cnpq???: CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
???metadata.dc.language???: por
???metadata.dc.publisher.country???: BR
Publisher: Universidade de Passo Fundo
???metadata.dc.publisher.initials???: UPF
???metadata.dc.publisher.department???: Ciências da Saúde e Ciências Biológicas
???metadata.dc.publisher.program???: Programa de Pós-Graduação em Odontologia
Citation: MEIRELLES, Potira Dalques. Porcelain cooling influence with and without leucite in reference to fracture systems infrastructure Zirconia. 2015. 106 f. Dissertação (Mestrado em Ciências da Saúde e Ciências Biológicas) - Universidade de Passo Fundo, Passo Fundo, 2015.
???metadata.dc.rights???: Acesso Aberto
URI: http://10.0.217.128:8080/jspui/handle/tede/815
Issue Date: 20-Mar-2015
Appears in Collections:Programa de Pós-Graduação em Odontologia

Files in This Item:
File SizeFormat 
2015PotiraMeirelles.pdf663.79 kBAdobe PDFView/Open ???org.dspace.app.webui.jsptag.ItemTag.preview???


Items in TEDE are protected by copyright, with all rights reserved, unless otherwise indicated.