Title: Influência do uso do hipoclorito de cálcio na força de adesão imediata / mediata de cimento autoadesivo ao sustrato dentinário coronário e radicular
Other Titles: Influence of the use of calcium hypochlorite on the force of immediate adhesion / mediate of self-adhesive cement to the coronary and dentinal substrate
???metadata.dc.creator???: Schneider, Najua Ellen 
???metadata.dc.contributor.advisor1???: Souza, Matheus Albino
???metadata.dc.description.resumo???: Esta pesquisa avaliou o efeito de diferentes soluções para desproteinização da matriz orgânica dentinária na força de adesão do cimento autoadesivo à dentina, imediato e a longo prazo. Utilizando 40 terceiros molares humanos divididos em 4 grupos. G1MT- (controle) sem tratamento de superfície. G2MT- controle (+) ácido fosfórico a 37% por 20 s. G3MT- tratamento com NaOCl 10% por 30s. G4MT- tratamento com CaOCl 10 % por 30s. Todos os dentes receberam uma restauração em resina composta (3mm de altura) cimentada com U200. Após a restauração, as coroas foram seccionadas para obtenção de palitos de 1 mm2 de área e submetidos ao teste de microtração (MT). Para o ensaio de push out(PO) 40 incisivos superiores humanos foram utilizados. Os dentes foram divididos em grupos de acordo com o tratamento (G5Po, G6Po, G7Po e G8Po) descrito previamente. Após o preenchimento do conduto com U200, as raízes foram seccionadas para obtenção de discos de dentina de 1 mm de espessura as quais foram submetidas ao teste de PO. Dois dentes de cada grupo foram armazenados em água destilada durante 6 meses a 37º. Os valores obtidos nos testes de MT e PO foram expressos em Mpa e analisados estatisticamente pelo teste de ANOVA de 1 fator (p< 0.05). Realizado avaliação do padrão de fratura por microscopia óptica e eletrônica sendo que as falhas foram classificadas em adesivas, mistas e coesivas. Os valores MT não apresentaram tendência de queda como no PO, os tratamentos com os hipocloritos não interferiram na força de adesão.
Abstract: This study evaluated the effect of different solutions for deproteinization of dentin organic matrix in the bond strength of self-adhesive cement to dentin, immediate and long-term. Using 40 human third molars divided into 4 groups. G1MT- (control) without surface treatment. G2MTcontrol (+) 37% phosphoric acid for 20 sec. G3MT- treatment with NaOCl 10% for 30 seconds. G4MT- treatment CaOCl 10% for 30 seconds. All teeth received a restoration in composite resin (3mm high) cemented with U200. After restoration, the crowns were sectioned to obtain sticks of 1 mm2 area and submitted to microtensile test (MT). For the test push out (PO) 40 human maxillary incisors were used. The teeth were divided into groups according to treatment (G5Po, G6Po, G7Po and G8Po) described previously. After the filling of the U200 with the roots were sectioned to obtain 1 mm thick dentin disks which were subjected to the test. Two teeth of each group were stored in distilled water at 37 for 6 months. The values obtained in the MT and OP tests were expressed in MPa and statistically analyzed by ANOVA factor 1 (p <0.05). Conducted evaluation of the fracture pattern by light and electron microscopy is that the failures were classified as adhesive, mixed and cohesive. MT values showed no downward trend as the PO, the treatment with hypochlorite did not affect the bond strength. Key Words: deproteinization, calcium hypochlorite, self-adhesive cement
Keywords: Odontologia
Cimentos dentários
Materiais dentários
???metadata.dc.subject.cnpq???: CIENCIAS DA SAUDE::ODONTOLOGIA
???metadata.dc.language???: por
???metadata.dc.publisher.country???: Brasil
Publisher: Universidade de Passo Fundo
???metadata.dc.publisher.initials???: UPF
???metadata.dc.publisher.department???: Faculdade de Odontologia – FO
???metadata.dc.publisher.program???: Programa de Pós-Graduação em Odontologia
Citation: SCHNEIDER, Najua Ellen. Influência do uso do hipoclorito de cálcio na força de adesão imediata / mediata de cimento autoadesivo ao sustrato dentinário coronário e radicular. 2016. 106 f. Dissertação (Mestrado em Odontologia) - Universidade de Passo Fundo, Passo Fundo, RS, 2016.
???metadata.dc.rights???: Acesso Aberto
URI: http://tede.upf.br/jspui/handle/tede/1385
Issue Date: 15-Apr-2016
Appears in Collections:Programa de Pós-Graduação em Odontologia

Files in This Item:
File Description SizeFormat 
2016NajuaEllenSchmeider.pdfDissertação Najua Ellen Schneider1.22 MBAdobe PDFView/Open ???org.dspace.app.webui.jsptag.ItemTag.preview???


Items in TEDE are protected by copyright, with all rights reserved, unless otherwise indicated.