Title: Comportamento de fadiga de uma cerâmica de uma cerâmica à base de silicato comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia -
Other Titles: Fatigue behavior of a ceramic of a ceramic-based silicate fatigue behavior of a ceramic based on lithium silicate and zirconia -
???metadata.dc.creator???: Ottoni, Rodrigo 
???metadata.dc.contributor.advisor1???: Borba, Marcia
???metadata.dc.description.resumo???: Avaliar o comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia (ZLS - VITA Suprinity, Vita Zahnfabrik), utilizando os métodos boundary e staircase. Métodos: Foram confeccionadas cento e vinte e cinco barras de cerâmica ZLS com as dimensões de 18 mm x 4 mm x 1,2 mm. Trinta corpos-de-prova foram testados em flexão em três pontos utilizando uma máquina de ensaio universal, em água destilada a 37oC. Os dados de flexão foram analisados com estatística de Weibull. Noventa e cinco barras foram submetidas aos ensaios de fadiga cíclica pelos métodos boundary e staircase. Os ensaios de fadiga foram realizados em uma máquina de ciclagem pneumática, com uma frequência de 2 Hz, em água destilada a 37oC. Dois tempos de vida foram avaliados em cada método, 10³ e 104 ciclos. A dureza Vickers (HV) foi avaliada em um microdurômetro com uma carga de 4,9 N por 20 s. Foi realizada análise fractográfica e análise de EDS dos corpos-de-prova. Resultados: A ZLS obteve resistência flexural média de 178 MPa, módulo de Weibull de 4 e HV de 680 MPa. Após 103 ciclos, para ambos os métodos, houve uma degradação de 78% da resistência à flexão inicial. Não houve uma degradação significativa quando o tempo de ciclagem aumentou de 103 para 104 ciclos. Tanto para o método staircase como para o boundary, a resistência para uma probabilidade de falha de 50% (¿50%) após 103 ciclos foi de 39 MPa. Após 104 ciclos ¿50% foi de 34 MPa no método boundary e 37 MPa no método staircase. A origem das falhas foi localizada na superfície de tração dos corpos-de-prova. O EDS revelou a presença de 11,8% de zircônio na ZLS. Conclusão: A ZLS apresentou significativa degradação das propriedades mecânicas em fadiga. Houve uma boa concordância entre os dois métodos de fadiga investigados.
Abstract: To evaluate the fatigue behavior of zirconia-reinforced lithium silicate ceramic (ZLS - VITA Suprinity, Vita Zahnfabrik), using the boundary and staircase methods. Methods: One hundred and twenty five ZLS ceramic bars with the dimensions of 18 mm x 4 mm x 1.2 mm were produced. Thirty specimens were tested for three-point bending using a universal testing machine in 37oC distilled water. Flexural strength data were analysed using Weibull statistics. Ninety five bars were subjected to cyclic fatigue using boundary and staircase methods. Fatigue tests were performed on a pneumatic cycling machine with a frequency of 2 Hz in 37oC distilled water. Two lifetimes were evaluated in each method, 10³ and 104cycles. Vickers hardness (HV) was evaluated using a microdurometer with a load of 4.9 N for 20 s.Fractographic analysis and EDS analysis of the specimens were also performed. Results: ZLS obtained a mean flexural strength of 178 MPa, Weibull modulus of 4 and HV of 680 MPa. After 103 cycles, for both methods, there was a degradation of 78% of the initial flexural strength. There was no significant degradation when the cycling time increased from 103 to 104cycles. For both the staircase and boundary methods, the stress for a failure probability of 50% (50%) after 10 cycles was 39
Keywords: Odontologia
Cerâmica odontológica
Sistemas CAD/CAM
???metadata.dc.subject.cnpq???: CIENCIAS DA SAUDE::ODONTOLOGIA
???metadata.dc.language???: por
???metadata.dc.publisher.country???: Brasil
Publisher: Universidade de Passo Fundo
???metadata.dc.publisher.initials???: UPF
???metadata.dc.publisher.department???: Faculdade de Odontologia – FO
???metadata.dc.publisher.program???: Programa de Pós-Graduação em Odontologia
Citation: OTTONI, Rodrigo. Comportamento de fadiga de uma cerâmica de uma cerâmica à base de silicato comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia. 2017. 155 f. Dissertação (Mestrado em Odontologia) - Universidade de Passo Fundo, Passo Fundo, RS, 2017.
???metadata.dc.rights???: Acesso Aberto
URI: http://tede.upf.br/jspui/handle/tede/1384
Issue Date: 17-Mar-2017
Appears in Collections:Programa de Pós-Graduação em Odontologia

Files in This Item:
File Description SizeFormat 
2017RodrigoOttoni.pdfDissertação Rodrigo Ottoni2.15 MBAdobe PDFView/Open ???org.dspace.app.webui.jsptag.ItemTag.preview???


Items in TEDE are protected by copyright, with all rights reserved, unless otherwise indicated.