???metadata.dc.type???: | Dissertação |
Title: | Comportamento mecânico de cerâmicas parcialmente cristalinas submetidas à fadiga cíclica |
Other Titles: | Mechanical behavior of partially crystalline ceramics subjected to cyclic fatigue |
???metadata.dc.creator???: | Vicari, Carolina Barbosa |
???metadata.dc.contributor.advisor1???: | Borba, Márcia |
???metadata.dc.description.resumo???: | Objetivo: Avaliar o comportamento mecânico de duas cerâmicas parcialmente cristalinas, uma vitrocerâmica de leucita (IPS Empress® CAD), VL, e outra cerâmica vitrea à base de dissilicato de lítio (IPS e-max® CAD), VD, submetidas ao ensaio de fadiga cíclica. Material e Método: Foram confeccionadas 70 barras de cada tipo de cerâmica com as dimensões de 16 mm x 4 mm x 1,2 mm, a partir do corte de blocos pré-fabricados de CAD-CAM. Para cada grupo, trinta corpos-de-prova foram testados através do teste de flexão em três pontos em uma máquina de ensaios universal e 40 corpos-de-prova foram submetidos ao ensaio de fadiga cíclica. O ensaio de fadiga cíclica foi realizado utilizando a técnica boundary, com frequência de 1 Hz, em água destilada a 37º C, em uma máquina de ciclagem pneumática. Foi realizada a análise fractográfica dos corpos-de-prova em microscópio eletrônico de varredura. Os dados foram analisados estatisticamente através da Análise de Weibull e teste de Mann-Whitney (¿=0,05). Resultados: O grupo VD (244 MPa) apresentou valor de resistência à flexão estatisticamente superior ao grupo VL (122 MPa). Porém, o grupo VL obteve maior módulo de Weibull. Ambos os grupos apresentaram uma redução de, aproximadamente 60%, da resistência à flexão inicial após a ciclagem por 104 ciclos. Nos testes de fadiga cíclica, para o grupo VD, não houve degradação da resistência à flexão com o aumento do número de ciclos (104 para 105). O grupo VL mostrou uma diminuição dos valores de resistência de 17% quando o tempo de ciclagem foi aumentado de 103 para 104 ciclos. Foram estimados valores de resistência à flexão para uma probabilidade de falha de 5% de 36 MPa para o grupo VL e 58 MPa para o grupo VD, após o mesmo tempo de ciclagem (104 ciclos). Conclusão: A cerâmica vítrea à base de dissilicato de lítio apresenta comportamento mecânico e de fadiga superior do que a vitrocerâmica de leucita, apesar da menor confiabilidade. Ainda, a ciclagem mecânica em meio úmido mostrou-se um fator significante na degradação das propriedades mecânicas das cerâmicas. |
Abstract: | Objective: To evaluate the mechanical behavior of two partially crystalline ceramics, a leucite-based glass-ceramic (IPS Empress® CAD), VL, and a lithium disilicate-based glass-ceramic (IPS e-max® CAD), VD, subjected to a cyclic fatigue test. Material and Methods: Seventy bar-shaped specimens were produced for each ceramic, with dimensions of 16 mm x 4 mm x 1.2 mm, by cutting pre-fabricated CAD-CAM blocks. For each group, thirty specimens were subjected to a three-point bending test in a universal testing machine and 40 specimens were subjected to cyclic fatigue test. The cyclic fatigue test was performed using the boundary technique with 1 Hz frequency, in 37 ° C distilled water using a pneumatic cycling machine. Fractographic analysis of the fractured specimens was performed with a scanning electron microscope (SEM). Data were statistically analyzed using the Weibull analysis and Mann-Whitney test (α = 0.05). Results: VD group (244 MPa) showed statistically superior flexural strength values than VL group (122 MPa). However, VL group obtained higher Weibull modulus. Both groups showed a reduction of, approximately, 60% of the initial flexural strength after cycling for 104 cycles. For VD group tested in fatigue, there was no degradation of the flexural strength values when the number of cycles was increased (104 to 105). VL group showed a decrease in strength of 17% when the number of cycles was increased from 103 to 104. Flexural strength values estimated for a probability of failure of 5% were 36 MPa, for VL group, and 58 MPa, for VD group, after the same number of cycles (104 cycles). Conclusion: Lithium disilicate-based glass-ceramic has superior mechanical and fatigue behavior than leucite-based glass-ceramic, besides its lower reliability. In addition, it can be concluded that mechanical cycling in humid conditions proved to be an important factor for the degradation of the mechanical properties of ceramics. |
Keywords: | Odontologia Cerâmica odontológica Fraturas Dentistry Dental ceramics Fractures |
???metadata.dc.subject.cnpq???: | CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA::ORTODONTIA |
???metadata.dc.language???: | por |
???metadata.dc.publisher.country???: | BR |
Publisher: | Universidade de Passo Fundo |
???metadata.dc.publisher.initials???: | UPF |
???metadata.dc.publisher.department???: | Ciências da Saúde e Ciências Biológicas |
???metadata.dc.publisher.program???: | Programa de Pós-Graduação em Odontologia |
Citation: | VICARI, Carolina Barbosa. Mechanical behavior of partially crystalline ceramics subjected to cyclic fatigue. 2015. 100 f. Dissertação (Mestrado em Ciências da Saúde e Ciências Biológicas) - Universidade de Passo Fundo, Passo Fundo, 2015. |
???metadata.dc.rights???: | Acesso Aberto |
URI: | http://10.0.217.128:8080/jspui/handle/tede/819 |
Issue Date: | 25-Feb-2015 |
Appears in Collections: | Programa de Pós-Graduação em Odontologia |
Files in This Item:
File | Size | Format | |
---|---|---|---|
2014CarolinaVicari.pdf | 1.67 MB | Adobe PDF | View/Open ???org.dspace.app.webui.jsptag.ItemTag.preview??? |
Items in TEDE are protected by copyright, with all rights reserved, unless otherwise indicated.