???metadata.dc.type???: | Dissertação |
Title: | Potencial da utilização de rejeito de minério de um ferro como precursor no desenvolvimento de um ligante álcali-ativado |
???metadata.dc.creator???: | Veiga, Fabiane Paschoal da ![]() |
???metadata.dc.contributor.advisor1???: | Prietto, Pedro Domingos Marques |
???metadata.dc.contributor.advisor-co1???: | Korf, Eduardo Pavan |
???metadata.dc.description.resumo???: | A produção de minério de ferro cresce a cada ano juntamente com o percentual econômico positivo que esse setor carrega para a economia no país. Em contrapartida, os desafios geotécnicos também crescem para a mineração. Responsável por grandes desastres ambientais que ocorreram nos últimos anos, esse setor necessita de alternativas que busquem solucionar a grande demanda de rejeitos oriundos do processo de beneficiamento do minério e que são dispostos em barragens. Com isso, o presente trabalho propôs o desenvolvimento de um aglomerante álcali ativado a partir de rejeito de minério de ferro. A metodologia proposta caracteriza-se na utilização do rejeito de minério de ferro como precursor, como fonte de cálcio a utilização de resíduo industrial cal de carbureto (CC) e como ativador silicato de sódio (SS). A Cura foi realizada por um período de 7 dias a temperatura de 23º C para aproximação a temperatura ambiente. As amostras testadas foram avaliadas através de Resistência a compressão simples e caracterizadas por Difratometria de Raio X (DRX), Espectroscopia no Infravermelho com Transformada de Fourier (FTIR), e lixiviação de metais. Foram estudados três percentuais de cal 5%, 7% e 10% e cinco concentrações de ativador 10%, 15%, 20%, 25% e 30%. Como resultados obteve -se a melhor resistência a compressão simples em 277,44 kPa ou 0,27 MPa, com a concentração de 10% de CC e 20% de SS, onde foi possível observar indícios de formação de géis CASH e NASH. Além disso, as amostras não apresentaram toxicidade e lixiviação de metais em níveis superiores aos parâmetros normativos analisados. |
Abstract: | Iron ore production grows every year, along with the positive economic percentage that this sector brings to the country's economy. On the other hand, geotechnical challenges also increase for mining. Responsible for major environmental disasters that have occurred in recent years, this sector needs alternatives that seek to solve the large demand for waste from the ore beneficiation process and which is disposed of in dams. Therefore, this work proposed the development of an activated alkali binder from iron ore waste. The proposed methodology is characterized by the use of iron ore waste as a precursor, the use of industrial waste carbide lime (CC) as a source of calcium, and sodium silicate (SS) as an activator. The curing was carried out for a period of 7 days at a temperature of 23°C to approximate room temperature. The tested samples were evaluated through simple compression strength and characterized by X-ray Diffractometry (XRD), Fourier Transform Infrared Spectroscopy (FTIR), and metal leaching. Three percentages of lime (5%, 7% and 10%) and five concentrations of activator (10%, 15%, 20%, 25% and 30%) were studied. As a result, the best simple compression strength was obtained at 277.44 kPa or 0.27 MPa, with the concentration of 10% CC and 20% SS, where it was possible to observe evidence of CASH and NASH gel formation. In addition, the samples did not present toxicity and metal leaching at levels higher than the normative parameters analyzed. |
Keywords: | Minérios de ferro Lixiviação |
???metadata.dc.subject.cnpq???: | ENGENHARIAS::ENGENHARIA CIVIL |
???metadata.dc.language???: | por |
???metadata.dc.publisher.country???: | Brasil |
Publisher: | Universidade de Passo Fundo |
???metadata.dc.publisher.initials???: | UPF |
???metadata.dc.publisher.department???: | Instituto de Tecnologia – ITEC |
???metadata.dc.publisher.program???: | Programa de Pós-Graduação em Engenharia Civil e Ambiental |
Citation: | VEIGA, Fabiane Paschoal da. Potencial da utilização de rejeito de minério de um ferro como precursor no desenvolvimento de um ligante álcali-ativado. 2023. 92 f. Dissertação (Mestrado em Engenharia Civil e Ambiental) - Universidade de Passo Fundo, Passo Fundo, RS, 2023. |
???metadata.dc.rights???: | Acesso Aberto |
URI: | http://tede.upf.br:8080/jspui/handle/tede/3002 |
Issue Date: | 28-Sep-2023 |
Appears in Collections: | Programa de Pós-Graduação em Engenharia Civil e Ambiental |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
2023FabianePaschoaldaVeiga.pdf | Dissertação Fabiane Paschoal da Veiga | 2.05 MB | Adobe PDF | View/Open ???org.dspace.app.webui.jsptag.ItemTag.preview??? |
Items in TEDE are protected by copyright, with all rights reserved, unless otherwise indicated.