???metadata.dc.type???: | Dissertação |
Title: | Avaliação do tratamento criogênico na microestrutura e propiredades mecânicas do aço AISI D6 |
Other Titles: | Evaluation of cryogenic treatment in microstructure and mechanical properties of AISI D6 steel |
???metadata.dc.creator???: | Silva, Matheus Borges da |
???metadata.dc.contributor.advisor1???: | Israel, Charles Leonardo |
???metadata.dc.description.resumo???: | Diversos estudos demonstram que o tratamento criogênico melhora as propriedades do aço ferramenta ao reduzir o percentual da austenita residual e promover a precipitação de carbonetos ultrafinos, proporcionando melhorias na estabilidade dimensional, ganho em tenacidade, resistência mecânica e desgaste. Porém, a bibliografia não discute de maneira clara e suficiente a influência do tempo de criogenia na mudança morfológica dos carbonetos, na dissolução percentual da austenita retida e sua influência nas propriedades mecânicas desta liga de maneira significativa. Neste estudo as amostras do aço AISI D6 foram caracterizadas por espectrometria, submetidos a tratamento térmico de têmpera em forno a vácuo, o tratamento térmico de revenimento anterior ao processo criogênico foi realizado igualmente em forno a vácuo, já os revenimentos posteriores a criogenia se deram em forno Mufla. Diferentes tempos de imersão no nitrogênio líquido, 2 e 24 horas foram realizadas em criogenia profunda a fim de avaliar variâncias nas propriedades que influenciam diretamente na aplicabilidade em alto rendimento dos facões de corte de chapas metálicas. Observou-se através das técnicas de microscopia óptica; MEV/EDS; DRX; Microdureza HV e Impacto Charpy que a temperatura de austenitização desempenha papel fundamental na criogenia, revelando que o tratamento criogênico atua no condicionamento da martensita formada na têmpera (martensita primária) e não na martensita formada a partir da transformação da AR, mostrou também que o tempo de imersão em criogenia profunda tem pouca influência nas propriedades específicas propostas pelo estudo, diferentemente da temperatura de austenitização, ponto chave para o propósito de aplicação do aço AISI D6 a facões de alto desempenho no corte de chapas metálicas. |
Abstract: | Several studies have demonstrated that cryogenic treatment improves the properties of tool steels by reducing the percentage of residual austenite and promoting the precipitation of ultrafine carbides, providing improvements in dimensional stability, toughness gain, mechanical strength and wear. However, the literature does not discuss clearly and sufficiently the influence of cryogenic time on the morphological change of the carbides and on the percentage dissolution of the retained austenite, and its influence on the mechanical properties of this alloy in a significant way. In this study the samples of the AISI D6 steel were characterized by spectrometry, submitted to heat treatment of tempering in a vacuum oven, the heat treatment of tempering prior to the cryogenic process was also carried out in a vacuum oven, the postventions after cryogenics were given in Mufla oven. Different times of immersion in liquid nitrogen, 2 and 24 hours were carried out in deep cryogenics in order to evaluate variances in the properties that directly influence the applicability in high yield of the cutting machetes of sheet metal. It was observed through the techniques of optical microscopy; MEV / EDS; DRX; Microhardness HV and Charpy Impact tests showed that the austenitization temperature plays a fundamental role in the cryogenics, revealing that the cryogenic treatment affects the martensite formed in the tempering (primary martensite) and not in the martensite formed from the AR transformation. immersion time in deep cryogenics has little influence on the specific properties proposed by the study, unlike the austenitizing temperature, point east, key for the purpose of application of AISI D6 steel to high performance machetes in the cutting of sheet metal. |
Keywords: | Aço Estruturas metálicas Metais - Corte |
???metadata.dc.subject.cnpq???: | ENGENHARIAS::ENGENHARIA MECANICA |
???metadata.dc.language???: | por |
???metadata.dc.publisher.country???: | Brasil |
Publisher: | Universidade de Passo Fundo |
???metadata.dc.publisher.initials???: | UPF |
???metadata.dc.publisher.department???: | Faculdade de Engenharia e Arquitetura – FEAR |
???metadata.dc.publisher.program???: | Programa de Pós-Graduação em Projeto e Processos de Fabricação |
Citation: | SILVA, Matheus Borges da. Avaliação do tratamento criogênico na microestrutura e propriedades mecânicas do aço AISI D6. 2018. 69 f. Dissertação (Mestrado em Projeto e Processos de Fabricação) - Universidade de Passo Fundo, Passo Fundo, RS, 2018. |
???metadata.dc.rights???: | Acesso Aberto |
URI: | http://tede.upf.br:8080/jspui/handle/tede/1855 |
Issue Date: | 12-Jan-2018 |
Appears in Collections: | Programa de Pós-Graduação em Projeto e Processos de Fabricação |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
2018MatheusBorgesdaSilva.pdf | Dissertação Matheus Borges da Silva | 4.5 MB | Adobe PDF | View/Open ???org.dspace.app.webui.jsptag.ItemTag.preview??? |
Items in TEDE are protected by copyright, with all rights reserved, unless otherwise indicated.