Title: Influência de diferentes substâncias químicas auxiliares na resistência de união de cimentos endodônticos à base de metacrilato à dentina radicular
???metadata.dc.creator???: Fuzinatto, Roger Nicolini 
???metadata.dc.contributor.advisor1???: Cecchin, Doglas
???metadata.dc.contributor.advisor-co1???: Souza, Matheus Albino
???metadata.dc.description.resumo???: O objetivo deste estudo foi avaliar a resistência de união de dois cimentos endodônticos à base de metacrilato, o Real Seal SE (Sybron Dental Specialties, Orange, CA, USA) e o EndoREZ (Ultradent Products Inc, South Jordan, UT, USA) à dentina radicular tratada com diferentes substâncias químicas auxiliares. Foram utilizados 60 dentes humanos unirradiculares. O preparo químico-cirúrgico foi realizado com instrumentos rotatórios de níquel-titânio ProTaper até o instrumento F5. As amostras foram tratadas com as diferentes substâncias químicas auxiliares, da seguinte forma: G1 (controle): soro fisiológico; G2: hipoclorito de sódio 5,25% (NaOCl) + EDTA 17%; G3: NaOCl + EDTA 17% + etanol 95%; G4: gel de clorexidina 2% (CHX) + EDTA 17%; G5: CHX + EDTA 17% + etanol 95%. Cada grupo foi aleatoriamente dividido em dois subgrupos, sendo que em um deles o cimento utilizado foi o EndoREZ e no outro o Real Seal SE. Depois de obturados, as raízes foram seccionados e o teste de push-out foi realizado. Para análise estatística foi realizado o ANOVA de dois fatores (cimento e tratamento de superfície) com nível de significância de 5%. Em relação à comparação entre as falhas dos cimentos, foi realizado o teste Qui-quadrado para verificar a associação entre os grupos experimentais e o tipo de falha observado. Os resultados mostraram que os maiores valores de resistência de união foram nos grupos preparados com CHX e etanol e obturados com o cimento Real Seal SE; nos grupos onde foi utilizado NaOCl os valores de resistência de união foram menores para o mesmo tipo de cimento. Para o cimento EndoREZ o NaOCl não diminuiu os valores de resistência de união comparado ao grupo controle porem os grupos que foi utilizado CHX tiveram melhores resultados Pode-se concluir que a substância química auxiliar utilizada no preparo dos canais radiculares interfere nos valores de resistência de união dos cimentos Real Seal SE e EndoREZ
Abstract: The aim of this study was to evaluate the bond strength of two methacrylate-based endodontic sealer, Real Seal SE (Sybron Dental Specialties, Orange, CA, USA) and EndoREZ (Ultradent Products Inc., South Jordan, UT, USA) to root dentin treated with different auxiliary chemical substances. Sixty single-rooted human teeth were used. The chemical-mechanical preparation was performed with rotary nickel-titanium instruments ProTaper until F5 instrument. The samples were treated with the different auxiliary chemicals, as follows: G1 (control): physiological saline, G2: 5.25% sodium hypochlorite (NaOCl) + 17% EDTA; G3: NaOCl + 17% EDTA + 95% ethanol, G4: 2% chlorhexidine gel (CHX) + 17% EDTA; G5: CHX +17% EDTA + 95% ethanol. Each group was randomly divided into two subgroups, in one of them EndoREZ cement was used and in the other Real Seal SE. Once obtured, the roots were cut and the push-out test was conducted. For statistical analysis was conducted the two-factor ANOVA (cement and surface treatment) with a significance level of 5%. Regarding the comparison between failures of cements, was held the Chi-square test to verify the association between experimental groups and the type of failure observed. The results have shown that the highest values of bond strength were in groups prepared with CHX and ethanol and obtured with the Real Seal SE sealer; in groups where NaOCl was used, values of bond strength were lower for the same type of sealer. To EndoREZ sealer the NaOCl did not decrease the bond strength values compared to control group, however that was used CHX had better results It can be concluded that the auxiliary chemical substance used in the preparation of root canals interferes with the values of bond strength of both Real Seal SE and EndoREZ sealer
Keywords: Endodontia
Obturação retrógrada
Materiais dentários
Endodontics
Retrograde filling
Dental materials
???metadata.dc.subject.cnpq???: CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA::ENDODONTIA
???metadata.dc.language???: por
???metadata.dc.publisher.country???: BR
Publisher: Universidade de Passo Fundo
???metadata.dc.publisher.initials???: UPF
???metadata.dc.publisher.department???: Ciências da Saúde e Ciências Biológicas
???metadata.dc.publisher.program???: Programa de Pós-Graduação em Odontologia
Citation: FUZINATTO, Roger Nicolini. Influência de diferentes substâncias químicas auxiliares na resistência de união de cimentos endodônticos à base de metacrilato à dentina radicular. 2014. 83 f. Dissertação (Mestrado em Ciências da Saúde e Ciências Biológicas) - Universidade de Passo Fundo, Passo Fundo, 2014.
???metadata.dc.rights???: Acesso Aberto
URI: http://10.0.217.128:8080/jspui/handle/tede/843
Issue Date: 29-May-2014
Appears in Collections:Programa de Pós-Graduação em Odontologia



Items in TEDE are protected by copyright, with all rights reserved, unless otherwise indicated.