Title: Influência da adição de fibras de polipropileno na resistência e na retração de um concreto compactado a rolo
???metadata.dc.creator???: Vecchia, Alessandro Fernandes Della 
???metadata.dc.contributor.advisor1???: Rosa, Francisco Dalla
???metadata.dc.contributor.advisor-co1???: Silveira, Adriana Augustin
???metadata.dc.description.resumo???: O presente trabalho buscou avaliar a influência de dois diferentes comprimentos de fibras de polipropileno adicionados ao CCR (Concreto Compactado com Rolo) no que diz respeito a sua resistência a compressão axial, compressão diametral e a retração sofrida pelo material durante sua cura e sua vida útil, para fins de utilização em base de pavimentação. Para atingir os objetivos do presente estudo, partiu-se da caracterização dos agregados, extraídos das regiões de Passo Fundo e de Osório no estado do Rio Grande do Sul. A caracterização avaliou a granulometria dos materiais individuais e a mistura ideal para tal compósito, além de verificação de propriedades físicas, tais como: Ensaios de Abrasão Los Angeles, absorção e massa específica. Para encontrar o teor de umidade o método utilizado foi o mesmo adotado em solos, ensaios de Proctor, com diferentes energias de compactação Após a caracterização foram moldados corpos-de-prova para verificar as resistências e a retração. As moldagens foram realizadas aleatoriamente de forma a obter maior confiabilidade nos resultados, diminuindo a influência de fatores externos. Para os ensaios de compressão axial e compressão diametral, foram moldados dezesseis betonadas de concreto com repetição, totalizando trinta e duas betonadas de concreto totalmente aleatorizadas. Para cada betonada foram moldados oito corpos-de-prova, para serem ensaiados quatro de compressão axial e quatro de compressão diametral. Os ensaios de retração foram executados com os melhores resultados dos ensaios anteriores, considerando os fatores que mais tiveram significância nos resultados de compressão, para esta análise, foram moldados três corpos-de-prova para cada mistura, totalizando três misturas diferentes e nove ensaios de retração. Finalizando-se o trabalho, nota-se uma influência maior do teor de cimento e da energia de compactação, obtendo-se resultados melhores os corpos-de-prova moldados com os maiores teores
Abstract: This work aims at evaluating the influence of two different lengths of polypropylene fibers which were added to the Roller-Compacted Concrete (RCC) on its resistance to axial compression, diametric compression, and retraction suffered by the material during its curing and useful life, so as to be used in the basis of paving. To attain the objectives of this study, there was a characterization of aggregates which were extracted from the cities of Passo Fundo and Osório in the state of Rio Grande do Sul, Brazil. The characterization evaluated the granulometry of the individual materials, and the ideal mix for such a composite, besides the checking of physical properties, such as Los Angeles Abrasion Test, absorption, and specific mass. To find moisture content, the method was the same one used in soils: Proctor Compaction Test, with different compaction energies. After the characterization, test specimens were molded to verify the resistances and the retraction. The moldings were made randomly so as to obtain higher reliability in the results, thus decreasing the influence of external factors. For axial compression tests, sixteen concrete mixes with repetition were molded, totalizing thirty two thoroughly randomized concrete mixes. For each concrete mix, eight test specimens were molded so there were four test specimens for axial compression and four test specimens for diametric compression. Retraction tests were performed with the best results of previous tests, considering the most significant factors of compression. For this analysis, three test specimens were molded for each mixture, totalizing three different mixtures and nine retraction tests. There is a greater influence of the cement proportion and of the compaction energy, thus the test specimens which were molded with a higher proportion had better results
Keywords: Concreto
Pavimentos de concreto
Rodovias - Projetos e construção
Concrete
Concrete floors
Highways - Projects and construction
???metadata.dc.subject.cnpq???: CNPQ::ENGENHARIAS::ENGENHARIA CIVIL::GEOTECNICA::PAVIMENTOS
???metadata.dc.language???: por
???metadata.dc.publisher.country???: BR
Publisher: Universidade de Passo Fundo
???metadata.dc.publisher.initials???: UPF
???metadata.dc.publisher.department???: Engenharias
???metadata.dc.publisher.program???: Programa de Pós-Graduação em Engenharia
Citation: VECCHIA, Alessandro Fernandes Della. Influência da adição de fibras de polipropileno na resistência e na retração de um concreto compactado a rolo. 2013. 94 f. Dissertação (Mestrado em Engenharias) - Universidade de Passo Fundo, Passo Fundo, 2013.
???metadata.dc.rights???: Acesso Aberto
URI: http://10.0.217.128:8080/jspui/handle/tede/324
Issue Date: 26-Apr-2013
Appears in Collections:Programa de Pós-Graduação em Engenharia Civil e Ambiental



Items in TEDE are protected by copyright, with all rights reserved, unless otherwise indicated.